What is Conveyor belt hot vulcanization jointing/ splicing?
All-In-One Portable Conveyor Belt Jointing Machine For Stainless
Steel Conveyor Belt Jointing The standard Conveyor Belt Hot Vulcanizing Joint used for all
types of conveyor belts excepting 2 to 8 ply. Itis the strongest and most reliable method of joining a belt and should
be used wherever possible, it is nearly as strong as the belt
itself is less troublesome than other fastening methods and results
in longer belt life. The surface is left smooth so that scrapers
and brushes can be used more effectively and with less risk of
damage to the belt than with a fastener joint. The belt is integrated, and the strength of the hot jointing can reach 80-90%. And it can prolong the life of conveyor accessories such as
belts, rollers and idlers.
How do you Vulcanize a conveyor belt?
Operation process of rubber layered conveyor belt hot vulcanized
joint compound
Take the 4-layer fabric conveyor belt as an example
Belt layering
The vulcanization length is 75cm, measure 60cm, divide it into 3
equal parts, peel it off in a trapezoid shape to expose the next
layer of fabric, and peel off the joints at the opposite sides
respectively.
To polish
Use an angle grinder to polish off the residual glue on the peeled
surface, lightly polish the fabric layer, and use an angle grinder
to polish the 10cm rubber into a rough surface. The rubber on the
front and back of the peeled side is also polished.
Apply hot vulcanized glue SK813 evenly on the polished surfaces of
the two joint fabrics
Rubberizing
Paste the hot vulcanized core glue evenly and flatly on the end
joint of the coated glue, lay several layers of core glue, lay glue
at the edge, cut the core glue into strips, and layer the layers to
ensure uniform, flat and compact.
Lay a certain thickness of hot vulcanized surface glue on the
polished surface of the joint surface.
Each layer of glue should be painted with hot vulcanized glue.
Vulcanization
The vulcanizer is placed flat, the steel beam is tightened with
screws, the conveyor belt joint is pressed after the pressing plate
is pressed, the heating plate is filled with water, heated to 145
℃, kept for 30 minutes, and the vulcanization is completed.
Machine specification of All-In-One Portable Conveyor Belt Jointing Machine For Stainless
Steel Conveyor Belt Jointing
| Model | Belt Width (mm) | Power(kw) | Dimensions (L*W*H mm) | Weight(kg) | Single Piece Weight(kg) |
|
| ZLJ-650*830 | 650 | 9.5 | 1370*830*630 | 430 | 45 |
| ZLJ-650*1000 | 10.8 | 1370*1000*630 | 500 | 66 |
| ZLJ-800*830 | 800 | 11.2 | 1520*830*630 | 535 | 70 |
| ZLJ-800*1000 | 13.5 | 1520*1000*630 | 575 | 79 |
| ZLJ-1000*830 | 1000 | 14.1 | 1720*830*630 | 595 | 82 |
| ZLJ-1000*1000 | 15.7 | 1720*1000*630 | 620 | 95 |
| ZLJ-1200*830 | 1200 | 16.5 | 1920*830*710 | 800 | 96 |
| ZLJ-1200*1000 | 17.2 | 1920*1000*710 | 870 | 113 |
| ZLJ-1400*830 | 1400 | 18.6 | 1930*830*760 | 930 | 107 |
| ZLJ-1400*1000 | 20.7 | 2120*1000*760 | 1180 | 132 |
| ZLJ-1600*830 | 1600 | 21.5 | 2320*830*800 | 1270 | 120 |
| ZLJ-1600*1000 | 22.3 | 2320*1000*800 | 1460 | 146 |
| ZLJ-1800*830 | 1800 | 23.3 | 2520*830*850 | 1380 | 137 |
| ZLJ-1800*1000 | 25.6 | 2520*1000*850 | 1650 | 164 |
| ZLJ-2000*830 | 2000 | 27.2 | 2720*830*950 | 1760 | 154 |
| ZLJ-2000*1000 | 30 | 2720*1000*950 | 1860 | 182 |
| ZLJ-2200*830 | 2200 | 29.2 | 2920*830*950 | 1860 | 165 |
| ZLJ-2200*1000 | 34.1 | 2920*1000*950 | 1970 | 198 |
Our Water Cooling System
use new designed water pressure bladder for pressurizing, it is made of rubber material, has better
performance and longer service life.
Package of All-In-One Portable Conveyor Belt Jointing Machine For Stainless
Steel Conveyor Belt Jointing
Please don't hesitate to contact us if you have any questions on
conveyor belt jointing questions.